The oxidation of TNM alloy at 700°C and 760°C — •Heng Zhang1,2 and Yongfeng Liang21Institute of Materials Physics, University of Münster, Germany — 2State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, China

The TNM sample morphology and components of the oxides are measured with SEM, EDS and XPS after oxidation until 200 hours at 700°C and 760°C respectively. Al2O3 is the main oxides at 700°C combined with a little TiO2, MoO2 and MoO3, while the oxides are TiO2,MoO2 and MoO3 at 760°C, exhibiting a good oxidation resistance under 700°C.