Bare surface structures and quantum dots growth on the GaAs(315)B surface — •Takayuki Suzuki, Yevgeniy Temko, Mingchun Xu, and Karl Jacobi — Fritz-Haber-Institut der Max-Planch-Gesellshaft, Faradayweg 4-6, 14195 Berlin

Surface structures of the GaAs(315)B surface were investigated under Ga- and As-rich conditions. The Ga-rich surface is not flat on atomic scale, but exhibits a very anisotropic surface morphology. Narrow stripes of 1×1 structure extend along [12-1]. The steps between the stripes often bunch together thus creating {101} facets. The As-rich surface is also not flat, but facets into vicinal (5 2 11)B surfaces with steps along the [13-1]proj. and [-321]proj.. {101} facets form on the sidewall of the steps along the [13-1]proj.. The GaAs(315)B surface becomes flat by adsorbing InAs with molecular beam epitaxy, and exhibits a c(2×2) reconstruction. Further adsorption induces quantum dots (QDs) formation. The QDs shape is given by {101}, {111}, and {2 5 11}A bounding facets. The size distribution of the QDs is quite broad, with the length at the foot ranging from 15 to 80 nm. Many QDs exhibit signs of coalescence. Stacking-faults and screw dislocations penetrating the QDs are directly detected with atomic resolution. Correlation between broad size distribution and incorporation of lattice defects are demonstrated experimentally for the first time.

100% | Mobil-Ansicht | English Version | Kontakt/Impressum/Datenschutz
DPG-Physik > DPG-Verhandlungen > 2004 > Regensburg