Effect of H2S treatment on the orientation and texture sharpness of MgO buffer layers on highly cube textured Ni-4at.%W tapes as a template for YBCO coated conductors — •Rainer Nast1, Bernhard Obst1, Oliver Stadel2, and Wilfried Goldacker11Forschungszentrum Karlsruhe, Institut für Technische Physik, Postfach 3640, D-76021 Karlsruhe — 2TU Braunschweig, Institut für Oberflächentechnik (IOT), Bienroder Weg 53, D-38108 Braunschweig

To achieve high current carrying capabilities in YBCO coated conductors based on cube textured metal substrates, the texture and stability of the buffer/metal interface is a necessary requirement. In this work cube textured Ni-4at.%W substrate tapes were subjected to different H2S treatments and the texture development of post-deposited MgO buffer layers was studied. The in-plane orientation and the texture sharpness of the MgO layers was found to depend strongly on the heat treatment time in Ar-10 ppm H2S. Increasing the time from 5 to 60 min at 800C changes the in-plane orientation from 45 over 0 to 45 at 15 min and the texture sharpens continuously to an FWHM (220) of < 6.

100% | Mobil-Ansicht | English Version | Kontakt/Impressum/Datenschutz
DPG-Physik > DPG-Verhandlungen > 2006 > Dresden