Grain boundary diffusion and segregation of 57Co in high-purity copper: Radiotracer measurements in B- and C-type diffusion regimes — •Daniel Gaertner, Gerhard Wilde, and Sergiy Divinski — Institute of Materials Physics, Westfälische Wilhelms-Universität Münster, Wilhelm-Klemm-Str. 10, 48149 Münster

Grain boundary diffusion of 57Co in high-purity polycrystalline copper is investigated using the radiotracer technique in Harrison’s B- (850−1150 K) and C-type (550−950 K) kinetic regimes. The triple product P=s·δ· Dgb (s is the segregation factor and δ the grain boundary width) and the grain boundary diffusion coefficient Dgb of Co in Cu are determined to obey the Arrhenius laws with the activation enthalpies of Qgb=66.2 kJ/mol and Hgb=100.9 kJ/mol, respectively. Using the experimental estimate of δ, δ ≅ 0.5 nm, Co is found to segregate strongly at Cu grain boundaries and the corresponding segregation factor follows an Arrhenius dependence with the segregation enthalpy of Hs=−34.7 kJ/mol . Co-diffusion experiments with the 57Co and 110mAg isotopes support a ’sub-interface’-type of grain boundary segregation of Co in Cu.

100% | Mobil-Ansicht | English Version | Kontakt/Impressum/Datenschutz
DPG-Physik > DPG-Verhandlungen > 2017 > Dresden