Phase transformations in mold-cast Nd-Fe(Co)-Al alloys — •G. Kumar1, J. Eckert1, S. Roth1, W. Löser1, S. Fähler1, H Hermann1, L. Schultz1, E. Garcia-Matrès2, and A. Wiedenmann21IFW Dresden, Helmholtz Strasse 20, D-01171 Dresden, Germany — 2Hahn-Meitner Institut Berlin, Glienicker Strasse 100, 14109 Berlin, Germany

Phase transformations in mold-cast Nd80−xFex (x = 15, 20, 25) and Nd60FexCo30−xAl10 (0 ≤ x ≤ 30) alloys were studied. The magnetic properties of as-cast and annealed samples were investigated with the help of a SQUID magnetometer and a pulse field of 50 T at different temperatures. The hard magnetic properties have been attributed to a metastable structure. Different characterization tools like XRD, SEM, TEM, and neutron scattering were used to study the structure and stoichiometry of the metastable phase. In addition, amorphous Nd80−xFex (x = 15, 20, 25) thin films were prepared by PLD method and the results were compared with the mold-cast bulk samples.

Acknowledgement

The work was supported by the German Science Foundation (DFG) via the DFG priority program No-dqPhasenumwandlungen in mehrkomponentigen SchmelzenNo-dqunder grant Ec 111/11-1.

100% | Bildschirmansicht | English Version | Kontakt/Impressum/Datenschutz
DPG-Physik > DPG-Verhandlungen > 2003 > Dresden