Optical and Magnetic Properties of Spinel Type Ferrites in Relation to their Crystallographic Order — •Vitaly Zviagin1, Paula Huth2, Chris Sturm1, Daniel Spemann3, Stephan Mändl3, Jörg Lenzner1, Annette Setzer1, Jan Meijer1, Reinhard Denecke2, Pablo Esquinazi1, Marius Grundmann1, and Rüdiger Schmidt-Grund11Universität Leipzig, Felix-Bloch-Institut für Festkörperphysik, Linnéstr. 5, Germany — 2Universität Leipzig, Wilhelm-Ostwald-Institut für Physikalische und Theoretische Chemie, Linnéstr. 2, Leipzig — 3Leibniz-Institut für Oberflächenmodifizierung e. V., Permoserstr. 15, Leipzig

ZnFe2O4 (ZFO) and composite ZnxFe3−xO4 thin films were fabricated on SrTiO3 (100) and TiN/MgO (100) substrates by pulsed laser deposition. Assigned electronic transitions in the dielectric function show a clear dependence on temperature as well as pressure during deposition and annealing processes. A decrease in the octahedral Fe2+ site occupancy with an increase in Zn concentration in composite films was observed in the band to band transition as well as the valence specific elemental composition, determined by spectroscopic ellipsometry and analysis of Fe 3p and 2p XPS core levels, respectively. Change in the ferrimagnetic response and electronic structure was examined after annealing ZFO films in argon and oxygen atmospheres at different temperatures as well as after irradiation by Ne+ ions with different fluences. Along with complementary methods such as Raman, AFM and SEM, we show the influence of crystallographic order on magnetic properties of normal, disordered and inverse spinel ferrite thin films.

100% | Mobil-Ansicht | English Version | Kontakt/Impressum/Datenschutz
DPG-Physik > DPG-Verhandlungen > 2018 > Berlin