CPP 39.9: Talk

Tuesday, March 17, 2020, 11:45–12:00, ZEU 114

Surface morphology of polyelectrolyte multilayer films with short PSS chains in water and air. Determining the surface elasticity of nanofilms — •Amir Azinfar1, Sven Neuber1, Jiří Vaněček2, Marie Vancová2,3, Jan Sterba2,3, Vítězslav Straňák3, and Christiane A. Helm11Institute of Physics - Angewandte Physik, University of Greifswald, Felix-Hausdorff-Str. 6, 17489 Greifswald, Germany — 2Institute of Parasitology, Biology Centre, Czech Academy of Sciences, Branisovska 31, 37005 Ceske Budejovice, Czech Republic — 3Faculty of Science, University of South Bohemia, Branisovska 1760, 37005 Ceske Budejovice, Czech Republic

We investigate the surface topology of polyelectrolyte multilayers made by sequential adsorption of polycations (PDADMA) and polyanions (low molecular weight PSS). We observed a buckling pattern of the film surface in air. The surface roughness σ(AFM) in air was always twice as high as in water. For PSS-terminated films, the periodicity of buckling patterns increased with the number of deposited layers from 185 nm to 225 nm. If the multilayer film was terminated with a PDADMA layer, the surface roughness σ(AFM) and the surface periodicity of buckling patterns were always bigger than for films terminated by a PSS layer. This is attributed to the larger surface coverage of PDADMA caused by its small linear charge density. We determined the surface elasticity of the film in non-linear and linear growth regimes by considering the surface strain and surface periodicity, and thus provide a model to explain the increase of periodicity with film thickness.