Phase selection and microstructural evolution of CoCrNi medium entropy alloy under cointernerless processing — •Angelo Fernandes Andreoli1, Olga Shuleshova1, Yuhao Wu1, 2, and Ivan Kaban11IFW Dresden, Institute for Complex Materials, Helmholtzstr. 20, 01069 Dresden, Germany — 2Department of Applied Physics, Northwestern Polytechnical University, Xi'an, 710072, China

The CoCrNi alloy was cointainerlessly processed using a portable electromagnetic levitation device where in-situ X-ray diffraction and a high-speed camera were used to monitor the phase evolution and solidification behavior. At low undercoolings, the alloy nucleates the stable γ-fcc phase, which consequently grows until the solidification is over. Beyond a critical undercooling, it first nucleates the metastable δ-bcc phase, which completely transforms into the stable γ-fcc phase as solidification evolves. Crystal growth kinetics were determined and are comparable to Fe-Co binary alloys. The microstructural evolution exhibits a transition from a dendritic microstructure at low undercoolings to an equiaxed-refined structure at deeper undercoolings.

100% | Mobil-Ansicht | English Version | Kontakt/Impressum/Datenschutz
DPG-Physik > DPG-Verhandlungen > 2020 > Dresden