NdFeB nanoparticles prepared by wet-milling — •Juliane Thielsch, Julia Lyubina, Thomas Woodcock, Ludwig Schultz, and Oliver Gutfleisch — IFW Dresden, P.O. Box 27 01 16, D-01171 Dresden

Since the prediction of a giant energy product of textured nanocomposite magnets [1] those materials where believed to be the next generation of permanent magnets. For effective exchange-coupling in such two-phase magnets grain sizes need to be in the range of the domain wall width of the hard magnetic phase. That makes a homogenous phase distribution and a microstructure with nanograins necessary. One option of preparing such materials is the synthesis of magnetic nanoparticles which further could be aligned and compacted to a bulk magnet. For this we performed wet-milling experiments of a NdFeGaNbB alloy. XRD studies revealed that by using a surfactant and a solvent during the high energy ball milling process amorphization sets in later than compared to dry milling experiments under the same conditions. Dynamic Light Scattering investigations showed a Gauss distribution of the particle size with a mean diameter of about 12nm which was also proven by TEM. Magnetic properties were measured with SQUID and showed so far rather poor coercivity values.

[1] R. Skomski and J.M.D. Coey, Phys. Rev. B, 1993, 48:15812

100% | Mobil-Ansicht | English Version | Kontakt/Impressum/Datenschutz
DPG-Physik > DPG-Verhandlungen > 2010 > Regensburg